Z. LI et al.: EFFECT OF THE ELECTROMAGNETIC COMPOUND FIELD ON THE GRAIN GROWTH ... 243–249 EFFECT OF THE ELECTROMAGNETIC COMPOUND FIELD ON THE GRAIN GROWTH AND WEAR RESISTANCE OF A Cu-Pb MONOTECTIC ALLOY VPLIV SESTA VLJENIH PULZIRAJO^IH IN ELEKTROMAGNETNIH POLJ NA RAST KRISTALNIH ZRN IN ODPORNOST Cu-Pb ENO-EVTEKTI^NE ZLITINE PROTI OBRABI Ziyang Li 1 , Ting Yu 1 , Dongxin Wang 2 , Guihong Geng 1* 1 College of Materials Science and Engineering, North Minzu University, Yinchuan 750021, China 2 State Key Laboratory of Special Rare Metal Materials, Northwest Rare Metal Materials Research Institute Ningxia Co.Ltd, Yejin Road 119, Shizuishan 753000, China Prejem rokopisa – received: 2019-05-29; sprejem za objavo – accepted for publication: 2019-09-30 doi:10.17222/mit.2019.115 The Cu-37.4w/%Pb (Cu-Pb) monotectic alloys were prepared under the normal solidification conditions and intense-pulse/ electromagnetic-compound fields. The Cu-Pb monotectic alloy prepared under the normal solidification conditions was mainly composed of -Cu and severely segregated Pb. With the compound fields applied, the segregation in the Cu-Pb alloy fabrication process could be eliminated. The alloy was composed of -Cu and -Pb, and its crystals were lath-shaped with much finer grains compared to the one fabricated under the normal conditions. In addition, the crystal grains grew along the tangential direction of the pulse current radiationally, from the guiding center to the surrounding area, caused by the Lorentz-force-induced gyroscopic motion. From the friction and wear experiments, the Cu-Pb alloy prepared by compound fields possesses a higher hardness, a lower friction coefficient and better wear resistance. Keywords: intense pulse and electromagnetic compound fields, Cu-37.4w/%Pb, Pb monotectic alloy, grain growth, wear resistance Avtorji ~lanka so pripravili eno-evtekti~no zlitino Cu-37,4 mas. % Pb (Cu-Pb) v normalnih pogojih strjevanja in v pogojih intenzivnih sestavljenih pulzirajo~ih elektromagnetnih polj. Eno-evtekti~na Cu-Pb zlitina, pripravljena v normalnih pogojih strjevanja, je bila v glavnem sestavljena iz -Cu in mo~no segregiranega Pb. Pri uporabi sestavljenih polj so odpravili segregacije Pb med izdelavo Cu-Pb zlitine. Zlitina je bila sestavljena iz homogenih trdnih raztopin -Cu in -Pb. Kristalna zrna so imela obliko letvic z mnogo bolj finimi kristalnimi zrni v primerjavi s tisto mikrostrukturo zlitine, ki je bila izdelana v normalnih pogojih strjevanja. Dodatno so ugotovili, da so kristalna zrna rasla vzdol` tangencialne smeri {irjenja tokovnih pulzov s sredi{~em vodenega preseka okolice, povzro~enih z Lorenzovo silo induciranega `iroskopskega gibanja. Preizkusi trenja in obrabe so pokazali, da ima Cu-Pb zlitina, pripravljena v sestavljenih poljih, ve~jo trdoto in manj{i koeficient trenja ter bolj{o odpornost proti obrabi. Klju~ne besede: intenzivna sestavljena pulzirajo~a in elektromagnetna polja, Cu-37,4 mas. % Pb, eno-evtekti~na zlitina, rast kristalnih zrn, odpornost proti obrabi 1 INTRODUCTION As one of the important metal materials in engineer- ing, monotectic alloys have many unique properties and are widely used. 1–7 Cu-Pb is a typical monotectic alloy, which has a high bearing capacity, a low friction coefficient and excellent wear/corrosion resistance. It has been widely used in thermal conduction and wear- resistant materials. However, the phase separation easily occurs during alloy preparation with normal solidi- fication due to the considerably large difference between the density of Cu and Pb. Thus strong segregation of the secondary phase and obvious stratification phenomenon exist in the Cu-Pb monotectic alloy, which results in substantial deterioration. Based on an understanding of biphasic separation mechanism, many new methods have been attempted to prepare monotectic alloys with excellent properties. Abramov prepared Al-Pb anti-friction alloys by casting in a microgravity field. It was found that the aluminum matrix produced a uniform distribution and possesses high anti-friction properties. 8 E. G. Wang and L. Zhang, 9 made research on the solidification structure of a Cu-80wt%Pb alloy, which was investigated under four different experimental conditions. The result showed that a magnetic field has a remarkable effect on restraining the gravity segregation of the Cu-Pb alloy. Y . Liu anal- yzed the liquid phase separating mechanism of immis- cible alloys and summarized the synthetic techniques of homogeneous immiscible alloys. 10 W. X. Hao 11 prepared Cu-37.4w/%Pb alloys in the highly undercooling conditions. It was found that the grain of the alloy was gradually refined with the increase of the cooling rate and the alloy showed a good anti-friction property. M. Materiali in tehnologije / Materials and technology 54 (2020) 2, 243–249 243 UDK 620.1:537:62-49:620.193.95 ISSN 1580-2949 Original scientific article/Izvirni znanstveni ~lanek MTAEC9, 54(2)243(2020) *Corresponding author's e-mail: gengguihong@163.com (Guihong Geng) Zhu 12 prepared Al-Pb-Cu alloy by mechanical alloying (MA), the result revealed the strength of the alloy was increased owing to solid-solution strengthening and precipitation strengthening. In addition, unidirectional solidification, stirring casting and rapid solidification are also widely used in the preparation of monotectic alloys. 10–15 In this paper the Cu-37.4w/%Pb (Cu-Pb) monotectic alloy was prepared by the intense pulse and electro- magnetic compound fields, where the undercooling and magnetostriction influence on the Cu-Pb monotectic alloy grain growth was investigated. Furthermore, the influence of the compound fields on the composition separation of the Cu-Pb monotectic alloy was analyzed and described. The refinement mechanism of the crystals under the compound fields was thoroughly investigated and explained. 2 EXPERIMENTAL PART The monotectic alloy ingots with the composition of Cu-37.4w/%Pb were prepared by a mixture of pure metals with a purity of 99.99 w/%. The ingot pre- parations were carried out in a simulated microgravity equipment that designed by us. Figure 1 is a schematic diagram of the device. 16 The temperature of the device was monitored by an infrared thermometer. The heating curve of the fabrication process was exemplified in Figure 2. The ingot prepared by normal solidification was heated to 1200 °C firstly, and then kept at 1200 °C for 60 min, followed by cooling to the room temperature. The ingot prepared from the intense pulse and electro- magnetic compound fields had the same heating process. After the temperature was held for 60 min, an electro- magnetic field (0.5 T) was applied for 2 min. In the cooling process at a temperature interval of 1200 °C to 955 °C, an intense pulse (with a width of 20 μs, frequency of 30 Hz and peak current of 1800A) was employed. After that, the Cu-Pb ingot was cooled to room temperature and cut into small pieces for the microstructure and properties investigation. The microstructures and compositions of the samples were investigated by scanning electron microscopy (SEM, SS-550 ISSEM), energy-dispersive spectroscopy (EDS, PHOENIX EDAX-2000) and X-ray diffraction (XRD, 6000X). Friction and wear experiments were per- formed on a HT-1000 friction-abrasion testing machine for 30 min at room temperature. The friction radius is 3 mm, the load is 5 N, and the rotation speed is 390 min –1 , samples were ground on GCr15 without lubrication. The microhardness tests were performed under a load of 4.9 N and a dwell time of 10 s. Z. LI et al.: EFFECT OF THE ELECTROMAGNETIC COMPOUND FIELD ON THE GRAIN GROWTH ... 244 Materiali in tehnologije / Materials and technology 54 (2020) 2, 243–249 Figure 1: Schematic diagram of our own designed equipment Figure 2: Curve of heating temperature 3 RESULTS 3.1 Microstructure of Cu-37.4w/%Pb monotectic alloy SEM images of the Cu-Pb monotectic alloy prepared under normal solidification and complex fields are shown in Figure 3, the EDS are shown in Figure 4 and the XRD patterns of the alloy are shown in Figure 5. As shown in Figures 4 and 5, a gray matrix denoted as -Cu could be observed, and the Pb-phase could be Z. LI et al.: EFFECT OF THE ELECTROMAGNETIC COMPOUND FIELD ON THE GRAIN GROWTH ... Materiali in tehnologije / Materials and technology 54 (2020) 2, 243–249 245 Figure 3: SEM of Cu-37.4w/%Pb, Cu-Pb alloy prepared under normal solidification (a and b) and complex fields (c and d). Transverse (a and c) and vertical (c and d) are the directions along and vertical to the current, respectively Figure 4: Energy-dispersive spectroscopy (EDS) images of Cu-37.4w/%Pb monotectic alloy, Cu-Pb alloy prepared under normal solidification condition (a) and complex fields (b) Figure 5: XRD patterns of the Cu-37.4w/%Pb monotectic alloy pre- pared under normal solidification conditions and complex fields distinguished at the crystal grain boundaries of the Cu. The Cu-Pb alloy prepared by normal solidification is mainly composed of -Cu and Pb with large crystal grains, in which the messily distributed Pb agglomerates on the matrix (Figure 3a and 3b). With the help of the intense pulse and electromagnetic compound fields, the segregation almost disappears, as shown in Figure 3c and 3d. The black-grid structure along the crystal grain boundary becomes lath-shaped, and the refined crystal grains are achieved. It is clear that the crystal grains radiationally grow from the guiding center to the surrounding area (Figure 3d). 3.2 Microhardness In the microhardness testing, 7 points were randomly selected for each sample. The results are presented in Table 1 (MAX T-L is the maximum difference). As shown in Table 1, the average microhardness of Cu-Pb under normal solidification is HV 4.9 35.47. Its microhardness is considerably increased to HV 4.9 58.50 due to the treatment by complex fields. The MAX T-L is large and the hardness is not uniform. Table 1: Microhardness test table of Cu-37.4w/%Pb (HV); MAX T-L is the maximum difference Test point Normal solidification Complex fields 1 37.88 57.10 2 36.24 57.07 3 35.65 61.24 4 42.29 57.49 5 33.80 55.30 6 35.84 63.37 7 26.58 57.90 Average 35.47 58.50 MAX T-L 15.71 8.07 3.3 Friction and wear properties The friction and wear properties of the alloy were evaluated using the friction coefficient. The variation of the friction coefficient with the time is shown in Fig- ure 6. The average friction of coefficient and the weight loss (30 min) of the alloy are shown in Table 2. It is obvious that the friction coefficient of the Cu-Pb alloy using normal solidification is stable after 10 minutes of testing, and its variation amplitude is larger compared with the one assisted by the complex field. Its average friction coefficient is 0.315, and the wear loss is 6.623 mg. The friction coefficient of the alloy prepared with complex fields needs 7 minutes for stabilization. Its average friction coefficient is 0.213, and the weight loss is substantially decreased by 51.5 %. Table 2: Friction coefficient and weight loss of Cu-Pb alloy Test sample Normal solidification Complex fields Average friction coefficient 0.315 0.213 Abrasion loss (mg) 6.623 3.210 4 DISCUSSION The Cu-Pb alloy is a kind of monotectic alloy. When the temperature of the Cu-Pb alloy is higher than the liquidus temperature, the liquid phase is completely miscible. As the liquid is cooled below to the liquidus temperature, the liquid phase separates into two phases (L 1 + L 2 ). When the Cu-Pb monotectic alloy is cooled below to the monotectic reaction temperature of 955 °C, a monotectic reaction occurs: L 1 (Cu) + L 2 (1) The liquid phase L 1 decomposes into a solid phase (Cu) and a liquid phase L 2 . The phase L 2 precipitates the surrounding (Cu). As the temperature continues to decline, the redistribution of the solute occurs in both (Cu) and L 2 phases. As a result, the rich-solute phase L 2 solidifies into a Pb-rich phase. As it is cooled to the eutectic temperature, the eutectic reaction occurs in the remaining liquid phase L 2 , forming two solid phases of Cu and Pb. L 2 Cu + Pb (2) Under normal solidification conditions the density difference between L 1 and L 2 in the Cu-Pb alloy is large, which leads to the phase stratification due to the Stockes deposition effect. As a result, severe phase segregation occurs due to gravity (Figure 3a and 3b). Without the electromagnetic field, the thermal move- ment of ions is random and arbitrary. As an electromag- netic field is applied (Figure 7), the velocity V of an ion is decomposed into two velocity components, i.e., per- pendicular V ⊥ and parallel V II . Along the vertical motion direction, the Lorentz force is produced because of the Z. LI et al.: EFFECT OF THE ELECTROMAGNETIC COMPOUND FIELD ON THE GRAIN GROWTH ... 246 Materiali in tehnologije / Materials and technology 54 (2020) 2, 243–249 Figure 6: Friction curves of the Cu-37.4w/%Pb monotectic alloy interaction between an ion with a charge of q and the electromagnetic field f: fB =× qv 1 (3) The velocity V ⊥ , without changes of the magnitude and the direction, is perpendicular to the Lorentz force. As a result, the ions rotate around the electromagnetic line with the load of the Lorentz force. Meanwhile, the force of V II results in the movement of the ions along the electromagnetic line. The influence of the electromag- netic field on a charged particle can be described by a motion Equation (4): mv q v B ( ) =× (4) Where m is the mass of the charged particle, the Larmor circle transformation of Equation 17,18 (4) is as follows in 19 : xx v yy v −− ⎛ ⎝ ⎜ ⎞ ⎠ ⎟ ⎡ ⎣ ⎢ ⎤ ⎦ ⎥ +−− ⎛ ⎝ ⎜ ⎞ ⎠ ⎟ ⎡ ⎣ ⎢ ⎤ ⊥⊥ 0 2 0 cc sin cos ⎦ ⎥ = == ⊥⊥ 2 22 2 22 vm v qB c (5) The particles move in the planezvtz =+ II 0 . Larmor’s center is: x v y v 00 −− ⎛ ⎝ ⎜ ⎞ ⎠ ⎟ ⊥⊥ cc sin cos and the guiding center is: rx v y v vtz c cc =− − + ⎛ ⎝ ⎜ ⎞ ⎠ ⎟ ⊥⊥ 000 sin cos II and the Larmor radius is: r vm v qB c == ⊥⊥ c The values of x 0 ,y 0 ,z 0 , V ⊥ , V II and are determined by the initial conditions. The Larmor radius, denoted as the cyclotron radius, is proportional to the ion mass and inversely proportional to the charge of q. Since the mass and charges of Cu + and Pb +4 are considerably different, the size of their Larmor radii is obviously different. The relative movement of the solute particles under the action of the electromagnetic field enhances the diffusion of the solute Pb in Cu, which results in an increase of the solubility of Pb in Cu, and therefore, the suppression of the segregation (Figure 3c and 3d). In the vertical direction of the pulse current, particles rotate in the plane Z. LI et al.: EFFECT OF THE ELECTROMAGNETIC COMPOUND FIELD ON THE GRAIN GROWTH ... Materiali in tehnologije / Materials and technology 54 (2020) 2, 243–249 247 Figure 8: Cooling curves of Cu-37.4w/%Pb monotectic alloys Figure 7: Magnetic effect under an energized coil zvtz =+ II 0 , where the crystal grains radiationally grow from the guiding center to the surrounding area (Figure 3d). In addition, the melt is repeatedly compressed via an electromagnetic force according to the magneto- strictive effect, which results in the rapid disappearance of the overheating in the melt. 19 Thus the degree of undercooling is substantially increased. Meanwhile, the growth of the crystal grains is suppressed, and the dendrites are broken. As a result, the crystal grains are refined and they become lath-shaped. According to the solidification theory, nucleation occurs in a melt under a certain condition of under- cooling to overcome the interface energy between the liquid and the solid phases. The intense pulse current can effectively increase the undercooling degree of the melt during solidification, which enhances the nucleation. As a pulse current is applied into a melt, the influence of the current on the undercooling degree can be expressed as, ΔΔ Tk JrTC m = − 0 22 1 π (6) where T is the melt undercooling, and J 0 is the current density before nucleation, and V is the nucleation vol- ume, and T m is the melting point, and r is the spheroidal radius, and k is a constant associated with the spherical coordinates, and c is the mass heat capacity, and is the correlation coefficient of electroconductivity. 19–21 Figure 8 shows the cooling curves for the Cu-37.4w/%Pb monotectic alloys. With a calculation, the T of Cu-Pb monotectic alloy substantially increases from 44 °C to 159 °C due to the treatment of complex fields, which is attributed to the enhancement of the nucleation and the refinement of the crystal grains. Under normal solidification, the phase segregation is strong, and lots of large blocks of Pb are observed (Fig- ure 3a and 3b). The hardness difference between the Pb and the Cu-Pb alloy is considerable, which results in the obviously inhomogeneous distribution of the micro- hardness (Table 1). The improvement of the micro- hardness, due to the treatment of complex fields, results in the solution strengthening. The solid solubility of Pb in Cu is considerably increased. Furthermore, intense pulse results in the refinement of the crystal grains, which is attributed to the homogeneous distribution of the microhardness (Table 1). The dissolution of Pb in the Cu matrix promotes the lubrication effect of the Cu-Pb alloy. Furthermore, the suppression of the phase separation and the refinement of crystals are beneficial to the wear resistance. Under the normal solidification, phase segregation is strong and the grains are coarse, where the friction coefficient is high and the amplitude of the friction coefficient is large (Figure 6). However, under the complex fields, the improvement of the microhardness and the refinement of crystals result in a considerably decrease of the friction coefficient and a small amplitude of the friction coeffi- cient (Figure 6). Thus, the wear resistance of the alloy is greatly improved (Table 2). 5 CONCLUSIONS 1) Under normal solidification, phase segregation in the Cu-Pb monotectic alloy is strong, and the crystal grains are coarse, which leads to a low microhardness and poor wear resistance. 2) Under the intense pulse and electromagnetic complex fields, the phase separation in the Cu-Pb monotectic alloy is considerably suppressed, and the crystals are refined. The crystal grains radiationally grow from the guiding center to the surrounding area due to the gyroscopic motion caused by the Lorentz force. 3) Under the same friction condition, the hardness is considerably increased by 64.93 %, and the weight loss of the Cu-Pb alloy prepared by the complex fields is substantially reduced by 51.5 %, which indicates that the wear resistance is greatly improved. Acknowledgements This project was financially supported by the National Natural Science Foundation of China (Grant No. 51561001) and the State Key Laboratory of Special Rare Metal Materials. 6 REFERENCES 1 L. Ratke, S. Diefenbach, Liquid immiscible alloys, Materials Science & Engineering R: Reports, 15 (1995) 7–8, 263–347, doi:10.1016/ 0927-796x(95)00180-8 2 Gouthama, G. B. Rudrakshi, S. N. Ojha, Spray forming and wear characteristics of liquid immiscible alloys, Journal of Materials Processing Technology, 189 (2007) 1–3, 224–230, doi:10.1016/ j.jmatprotec.2007.01.026 3 K. X. Song, Y. J. Zhou, P. F. Zhao, Y. M. Zhang, N. Bai, Cu-10Sn-4Ni-3Pb alloy prepared by crystallization under pressure: An experimental study, Acta Metallurgica Sinica, 26 (2013)2 , 199–205, doi:10.1007/s40195-012-0118-0 4 L. F. Kolesnichenko, O. I. Fushchich, L. D. Ignatenko, A. Yu. Talochka, S. V . Chernyauskas, Structure formation in the Cu-Sn-Pb system during sintering, Translated from Poroshkovaya Metallurgiya, 5( 1986) 281, 28–34, doi:10.1007/BF00813949 5 Y . Liu, J. J. Guo, Y . Q. Su, H. S. Ding, J. Jia, Microstructures of rapidly solidified Al-In immiscible alloy, Transactions of Nonferrous Metals Society of China, 11 (2001) 1, 84–89, doi:10.1034/j.1600- 0692.2001.300107. x 6 Y . F. Wang, H. Y . Gao, Y . F. Hana, Y . B. Dai, J. Wang, B. D. Sun, First-principles study on the solubility of iron in dilute Cu-Fe-X alloys, Journal of Alloys and Compounds, 691 (2016), 992–996, doi:10.1016/j.jallcom.2016.08.247 7 P. Terizieff, R. Luck, Magnetic investigations in liquid Al-In. Journal of Alloys and Compounds, 360 (2003) 1–2, 205–209, doi:10.1016/s0925-8388(03)00347-5 8 O. V . Abramov, N. A. Bushe, T. F. Markova, D. Y . Chashechkina, Al-Pb antifriction alloys produced under conditions of compensation of gravitational segregation by electromagnetic forces, Metal Science & Heat Treatment, 24 (1982) 4, 239–243, doi:10.1007/BF00772466 9 E. G. Wang, L. Zhang, X. W. Zuo, et al. Morphology of the Cu-rich Phase in Cu-Pb Hypermonotectic Alloys under an Intense Magnetic Field, Steel Research International, 78 (2007) 5, 386–390, doi:10.1002/srin.200705908 10 Y . Liu, Y . X. Li, J. J. Guo, Liquid phase separating mechanism and preparation techniques of immiscible alloys. Transactions of Non- ferrous Society of China, 12 (2002) 3, 357–365, doi:10.1179/ 136217102225002655 Z. LI et al.: EFFECT OF THE ELECTROMAGNETIC COMPOUND FIELD ON THE GRAIN GROWTH ... 248 Materiali in tehnologije / Materials and technology 54 (2020) 2, 243–249 11 W. X. Hao, G. C. Yang, H. Xie, Solidification behavior and micro- structure of deep supercooled cu-37.4% Pb monotectic alloy, Foundry Technology, 25 (2004) 2, 105–107, doi:10.3969/j.issn. 1000-8365.2004.07.022 12 M. Zhu, M. Q. Zeng, Y . Gao, Microstructure and wear properties of Al-Pb-Cu alloys prepared by mechanical alloying, Wear, 253 (2005) 7, 832–838 13 B. Majumdar, K. Chattopadhyay, Aligned monotectic growth in unidirectionally solidified Zn-Bi alloys, Metallurgical and Materials Transactions A (Physical Metallurgy and, Materials Science), 31 (2000), 1833–1842, doi:10.1007/s11661-006-0245-1 14 S. T. Ashok, T. V. Rajan, Bearing characteristics of cast leaded aluminium-silicon alloys, Wear, 197 (1996), 105–114, doi:10.1016/ 0043-1648(95)06861-9 15 J. B. Andrews, A. C. Sandlin, R. A. Merrick, Directional solidifi- cation in immiscible systems: The influence of gravity, Advances in Space Research, 11 (1991), 291–295, doi:10.1016/0273-1177(91) 90298-x 16 A. Kamio, S. Kumai, H. Tezuka, Solidification structure of mono- tectic alloys, Materials Science & Engineering A, 146 (1991) 1–2, 105–121, doi:10.1016/0921-5093(91)90271-N 17 Z. A. Tian, L. L. Zhou, Y . F. Mo, Y . C. Liang, R. S. Liu, Cooling rate dependence of polymorph selection during rapid solidification of liquid metal zinc, Transactions of Nonferrous Metals Society of China, 25 (2015) 12, 4072–4079, doi:10.1016/S1003-6326(15) 64057-2 18 Z. J. Yan, J. Yan, Y Hu, et al, Crystallization in Zr60Al15Ni25bulk metallic glass subjected to rolling at room temperature, Science in China Series E: Technological Sciences, 53 (2010) 1, 278–283, doi:10.1007/s11431-009-0315-x 19 J. Z. Zhao, L. Ratke, B. Feuerbacher, Microstructure evolution of immiscible alloys during cooling through the miscibility gap, Modelling and Simulation in Materials Science, 6 (1998)2 , 123–139, doi:10.1088/0965-0393/6/2/003 20 D. A. Da, W. S. Jiang, A New Method for Procession Monotectic Alloys under Simulated Microgravity Condition Using Electro-Mag- netic Field on Earth. 4th International Conference on Experimental Methods for Microgravity Materials Science Research, California, 1992 21 J. Y . Xu, S. X. Jin. Physic of plasma. Beijing: atomic energy press, 1981, 63-70 22 C. Y . Ban, Fundamental study on solidification of Al alloys under electromagnetic fields, Northeastern University, 2002 23 M. Zhang, Study solidification microstructure characteristics of Fe-Based alloys subjected to pulsed electric current treatment, Yanshan University, 2006 24 J. P. Barnak, A.F. Sprecher, H. Conrad. Colony (grain) Size Reduc- tion in Eutectic Pb-Sn Castings by Electroplusing, Scripta Metallurgica Et Materialia, 32 (1995) 6, 879–884, doi:10.1016/0956- 716X(95)93218-S 25 Y . H. Zhou, Z. Q. Hu, W. Q. Jie, Solidification technology, Beijing: machinery industry press, 1998 Z. LI et al.: EFFECT OF THE ELECTROMAGNETIC COMPOUND FIELD ON THE GRAIN GROWTH ... Materiali in tehnologije / Materials and technology 54 (2020) 2, 243–249 249